KATANA* Zirconia UTML

Ultra translucent zirconium dioxide with color graduation for natural aesthetics in the anterior region

  • Ideal for restorations in the anterior region
  • Above-average translucency for natural aesthetics
  • 4 layer Multicolor with flowing layer transition
  • Available in 16 VITA* classical shades A-D
  • Multicolor for monolithic restorations and microveneering
  • Anterior bridge frames up to 3 units with one pontic

Indications

  • Fully anatomical crowns and bridges with up to 3 units and up to one pontics in the anterior region
  • Crowns and bridge frames for partially veneered solutions with up to 3 units and up to one pontics in the anterior region
  • Inlays, onlays, partial crowns and veneers
Color rangeA1A2A3A3,5A4B1B2B3B4
C1C2C3C4D2D3D4

Recommendations for colour selection can be found in the product flyer.

Technical specifications
Chemical composition  
Zirconium dioxide (ZrO2) & Hafnium oxide (HfO2) 87 – 92 %
Yttrium oxide (Y2O3) 8 – 11%
Other oxides and pigments 0 – 2 %
Technical specifications  
3-point bending strength 557 MPa
Coefficient of thermal expansion 9.7 10 -6 / K-1
Translucency 43 %
Hardness 1,280 HV10
E-module 214–217 GPa