KATANA* Zirconia YML
The functional and aesthetic flagship of the Katana series with outstanding dental aesthetics and universal applicability
- Latest generation of type-layer zirconia with patented raw material technology
- Consistently highest flexural strength in the dentin and transfer area
- Optimum translucency with pigmented incisal layer for natural dental aesthetics
- 4 layer Multicolor with flowing layer transition
- Available in 13 VITA* classical shades A-D
- Multicolor for monolithic restorations and microveneering
- Bridge frames with up to 14 units and up to two adjacent pontics
- Implantat prosthetic abutments, monolithic abutment crowns and bridges
Indications
- Fully anatomical crowns and bridges with up to 14 units and up to two pontics
- Crowns and bridge frames for partially and fully veneered solutions with up to 14 units and up to two pontics
- CadAbut Duo (Two-piece abutments)
- Dentin core crowns and bridges according to Josef Schwaiger (Patent: EP2363094B1/DE102010002484B4)
Chemical composition | |
---|---|
Zirconium dioxide (ZrO2) & Hafnium oxide (HfO2) | 87–95 % |
Yttrium oxide (Y2O3) | 5–10 % |
Other oxides and pigments | 0–2 % |
Technical properties | |
---|---|
3-point bending strength | 750 – 1,100 MPa |
Coefficient of thermal expansion | 10.1 10-6 K-1 |
Translucency | 45 – 49 % |
Hardness | 1,255 HV10 |
E-module | 214–217 GPa |