KATANA* Zirconia UTML
Ultra translucent zirconium dioxide with color graduation for natural aesthetics in the anterior region
- Ideal for restorations in the anterior region
- Above-average translucency for natural aesthetics
- 4 layer Multicolor with flowing layer transition
- Available in 16 VITA* classical shades A-D
- Multicolor for monolithic restorations and microveneering
- Anterior bridge frames up to 3 units with one pontic
Indications
- Fully anatomical crowns and bridges with up to 3 units and up to one pontics in the anterior region
- Crowns and bridge frames for partially veneered solutions with up to 3 units and up to one pontics in the anterior region
- Inlays, onlays, partial crowns and veneers
| Color range | A1 | A2 | A3 | A3,5 | A4 | B1 | B2 | B3 | B4 |
| C1 | C2 | C3 | C4 | D2 | D3 | D4 |
Recommendations for colour selection can be found in the product flyer.
| Chemical composition | |
|---|---|
| Zirconium dioxide (ZrO2) & Hafnium oxide (HfO2) | 87 – 92 % |
| Yttrium oxide (Y2O3) | 8 – 11% |
| Other oxides and pigments | 0 – 2 % |
| Technical specifications | |
|---|---|
| 3-point bending strength | 557 MPa |
| Coefficient of thermal expansion | 9.7 10 -6 / K-1 |
| Translucency | 43 % |
| Hardness | 1,280 HV10 |
| E-module | 214–217 GPa |
Contact
Downloads
Manufacturer information
- Technical Guide KATANA™ ZirconiaMulti-layered Series
Informazioni sul fabbricante
- Manuale tecnico KATANA™ ZirconiaMulti-layered Series
* This symbol is a commercial designation/registered trademark of a company which is not part of the BEGO company group.
Pictures and illustrations are exemplary. Colors, symbols, design, and information on the labels and/or packaging shown may differ from reality.